[[File:Rfcllw.jpg|缩略图|300px|[https://image.baidu.com/search/detail?ct=503316480&z=0&ipn=d&word=热处理裂纹的分类&step_word=&hs=0&pn=19&spn=0&di=2760&pi=0&rn=1&tn=baiduimagedetail&is=0%2C0&istype=2&ie=utf-8&oe=utf-8&in=&cl=2&lm=-1&st=-1&cs=2309490637%2C3522574599&os=3172459406%2C820768934&simid=3315412447%2C271576869&adpicid=0&lpn=0&ln=1576&fr=&fmq=1582797936421_R&fm=result&ic=&s=undefined&hd=&latest=&copyright=&se=&sme=&tab=0&width=&height=&face=undefined&ist=&jit=&cg=&bdtype=15&oriquery=&objurl=http%3A%2F%2Fi.serengeseba.com%2Fuploads%2Fi_5_3784059333x1402461282_26.jpg&fromurl=ippr_z2C%24qAzdH3FAzdH3Fooo_z%26e3Bfj6jg2jfjkw_z%26e3Bv54AzdH3FoAzdH3F%25El%25BD%25BF%25Eb%25BD%25AE%25El%25BD%25BF%25Ec%25la%25l8%25Ec%25b8%25bF%25Ec%25la%25l8%25E9%25Bb%25ba%25Eb%25BE%25Bl%25Em%25lb%25AF%25E9%25BB%25ba%25E9%25Bl%25bb%25El%25l0%25AE%25El%25Ad%25lbAzdH3F&gsm=14&rpstart=0&rpnum=0&islist=&querylist=&force=undefined 原圖鏈接][http://www.serengeseba.com/w/齿轮齿向偏向一边是什么问题/ 图片来源]]] 
'''热处理裂纹的分类'''：钢件[[淬火]]时一旦产生宏观裂纹就将报废，造成材料、加工费用的损失。弄清淬火裂纹的形态，分析其产生的原因，并从微观上研究其形成机制及过程，掌握其规律性，对于探寻防止淬裂的方法和措施，无疑具有重要意义。<ref>[http://www.aitmy.com/news/201709/22/news_216677.html  常见的热处理裂纹基本类型],百度文库，2017年9月22日</ref>

常见的热处理裂纹基本类型：[[纵裂]]（组织应力型）、[[弧裂]]（局部拉应力型）、大型工件淬火裂纹（纵断、横断）、边廓表面裂纹（局部拉应力型）、[[脱裂]]、第二类应力裂纹。

热处理中发现的裂纹多数是出现在淬火之后。有些是在淬火前已经形成了裂纹,只是在淬火后裂纹扩展了才看清楚。淬火裂纹是在塑性变形难以进行的条件下内应力超过了破断抗力时产生的。